Reversible and irreversible expansion in construction
Contents |
[edit] Introduction
Most building materials suffer movements which can be caused by changes in temperature, changes in moisture content, subsidence and so on. Porous building materials, for example, can suffer from sudden changes to their original moisture content. In some materials, this sudden change can occur immediately after the process of manufacture and can continue during storage and distribution; it will depend on the properties of the material.
Changes can include expansion, contraction, deformation and so on and can sometimes lead to problems such as cracking and water penetration, or even failure.
Very broadly, expansion can be either reversible or irreversible.
[edit] Irreversible expansion
As an example of irreversible expansion, due to the intense heat involved, newly-fired clay bricks will be very dry as they emerge from the kiln. Their very low moisture content combined with sudden exposure to the atmosphere will mean they can absorb moisture from the air until they have reached a point of normal or atmospheric moisture level. This increase in moisture content causes expansion of the brick which is irreversible: the brick is marginally larger than when it was originally formed and will not shrink back to its original size.
Irreversible expansion can also be seen in calcium silicate bricks (made from mainly sand, lime and quartz). Formed in an autoclave under high heat, moisture and pressure, they are more saturated than clay bricks and after the process will immediately shrink until they have reached a moisture content that is in equilibrium with the of the prevailing air.
In both cases, before newly manufactured bricks are used on site, time is usually allowed for this irreversible expansion to be completed, otherwise cracking may occur if they are used immediately. In many cases, this is achieved by the time taken to store and distribute the bricks to the end user.
[edit] Reversible expansion
Reversible expansion usually occurs as a result of moisture absorption when materials are in use, e.g on a building in an exposed location. The material may expand when wet and contract as it dries out. This cycle may be repeated for the life of the material and can be accommodated with the correct provision of movement joints.
Thermal expansion may also be reversible. For example, metals will tend to expand when they become hot and contract when they cool.
For more information see: Thermal expansion.
Moisture present in buildings may freeze during cold weather, expanding as the water turns to ice, then thawing as temperatures increase. This repeated freeze-thaw cycle can result in significant damage, such as cracking brickwork, bursting pipes and so on.
For more information see: Frost attack.
[edit] Related articles on Designing Buildings Wiki
- Cracking in buildings.
- Defects in brickwork.
- Defects in construction.
- Defects in stonework.
- Frost attack.
- Ground heave.
- Latent defects.
- Leaning Tower of Pisa.
- Movement joint.
- Preventing wall collapse.
- Settlement.
- Sinkholes.
- Subsidence.
- Thermal expansion.
- Underpinning.
- Why do buildings crack? (DG 361).
Featured articles and news
BSRIA Briefing 2024: Sustainable Futures speakers
Redefining Retrofit for Net Zero Living 22 Nov.
Wall of support for post-Grenfell regulation of electricians
Call for a shake-up of the construction industry highlighted on radio.
Digital sustainability through future AEC tools
Bringing together industry and academia to meet challenges.
Skills gap for net zero highlighted to Minister for Industry
ECA convenes roundtable discussion at Portcullis House.
Evidencing Net Zero with the new UK buildings standard
Pilot version with detailed excel proforma out now!
Scottish Building Safety Levy, in consultation
From direct remediation and the RPDT, to the costs and alternatives.
Waves of warmer homes grants for the rental sector
Boosting energy efficiency standards for all rented homes.
A refocus of the National Planning Policy Framework
Key terms described in brief, as the consultation closes the evening of the 24th.
Fortified farmhouses of the unruly 16th-and 17th-century borders.
ECA shares advice for those who may be exposed to risks.
How to revolutionise UK housing with MMC
CIC and Supply Chain Sustainability School unveil a plan.
From the UKs largest manufacturer and supplier of lime.
From mud bricks to smart concrete
A brief history from 7000BC to a future on the moon.
Regulator of Social Housing publishes latest fire safety report
Covering remediation of 11 metre plus social housing sector buildings.
Apartment and Duplex Defects Remediation Bill 2024
Approved for priority drafting by Government of Ireland.
The long list with in the frame of key historical events.
Competence frameworks for sustainability in the built environment
Code of practice, core criteria consultation draft for comment.
New Floods Resilience Taskforce
With a wet met office autumn prediction.